A new copolymer based on hydrophobically modified Polyacrylamide was characterized by its rheological behavior. Viscosities were measured at various temperatures and salinities in comparison to a regular acrylamide/sodium acrylate copolymer (HPAM). It is proven that the viscosity of this new associative polymers increases with temperature, while the viscosity of HPAM is decreasing.

This effect was further explored in porous media studies. Polymer solution was injected into a Bentheimer sandstone with a permeability of around 2 Darcy at 20°C and the pressure drop was measured along the core. From the pressure drop the resistance factor, RF, was derived, which is a measure of the in-situ viscosity in the porous medium.

Next, the temperature was increased to 45°C. This resulted in an increase of the RF from 15 to 94. At 60°C a RF of even 152 was observed. By reducing the flow rate from 0.5 ml/min to 0.1 ml/min the RF could be further increased to 562. Finally the flow rate and the temperature were set to the initial values and a RF of 21 was measured, which shows that the thermothickening behavior of the novel polymer is reversible. Monitoring the effluent viscosity indicated that the increase of the RF / in-situ viscosity is due to polymer being retained in the porous media. This retained polymer lowers the permeability of the rock pores and thereby increases RF. By lowering the temperature the properties are switched back to the original state and the polymer is released from the rock matrix.

The thermothickening behavior of the discussed copolymer can be quite beneficial for polymer flooding applications. During injection at surface temperature the viscosity of the fluid is low and therefore it can be injected at high rates. Once the polymer solution migrates deeper into the reservoir formation, the temperature of the fluid will rise gradually; in-situ viscosity will increase and simultaneously the flow rate will decrease. Both effects will help to improve sweep efficiency.

In general, the magnitude of the RF can be adjusted by modifying the polymer structure and hence the copolymer can be optimized for specific field conditions.

© EAGE Publications BV
Loading

Article metrics loading...

/content/papers/10.3997/2214-4609.201700285
2017-04-24
2024-04-20

  • From This Site

    /content/papers/10.3997/2214-4609.201700285
    dcterms_title,dcterms_subject,pub_keyword
    -contentType:Journal -contentType:Contributor -contentType:Concept -contentType:Institution
    10
    5
Loading full text...

Full text loading...

References

  1. Dragan, S., Ghimici, L.
    [2001] Viscometric behaviour of some hydrophobically modified cationic polyelectrolytes. Polymer42, 2887–2891.
     [Google Scholar]
  2. Fedors, R.F.
    [1979] An equation suitable for describing the viscosity of dilute to moderately concentrated polymer solutions. Polymer20, 225–228.
     [Google Scholar]
  3. Frampton, H., Taylor, S.
    [2009] Gel Systems with Properties Suitable for Remediation of Water Injection Wells with Performance Impaired by Fractures and Super-Permeability Zones. Chemistry in the Oil Industry XI.
     [Google Scholar]
  4. L’Alloret, F., Maroy, P., Hourdet, D., Audebert, R.
    [1997] Reversible Thermoassociation of Water-soluble Polymers. Rev. Inst. Franc. Petr. 52, 117–128.
     [Google Scholar]
  5. Leblanc, T., Braun, O., Thomas, A., Divers, T., Gaillard, N., Favero, C.
    [2015] Rheological Properties of Stimuli-Responsive Polymers in Solution to Improve the Salinity and Temperature Performance of Polymer-Based Chemical Enhanced Oil Recovery Technologies. SPE 174618 presented at the SPE Enhanced Oil Recovery Conference, Kuala Lumpur, 11–13 August.
     [Google Scholar]
  6. Ma, J., Liang, B., Cui, P., Dai, H., Huang, R.
    [2003] Dilute solution properties of hydrophobically associating polyacrylamide: fitted by different equations. Polymer44, 1281–1286.
     [Google Scholar]
  7. Maia, A.M., Borsali, R., Balaban, R.C.
    [2009] Comparison between a polyacrylamide and a hydrophobically modified polyacrylamide flood in a sandstone core. Mat. Sci. Eng. C29, 505–509.
     [Google Scholar]
  8. McCormick, C. L., Johnson, C. B.
    [1986] Structurally Tailored Macromolecules for Mobility Control in Enhanced Oil Recovery. Water-Soluble Polymers for Petroleum Recovery edited by G.A.Stahl, D.N.Schulz, 161–180.
     [Google Scholar]
  9. Reichenbach-Klinke, R., Stavland, A., Zimmermann, T., Bittner, C. and Brodt, G.
    [2015] Copolymers for Polymer Flooding - Structure-performance Relationship in Porous Media, paper presented at the IOR 2015 – 18th European Symposium on Oil Recovery, Dresden, Germany, 14–16 April.
     [Google Scholar]
  10. Reichenbach-Klinke, R., Stavland, A., Zimmermann, T. and Brodt, G.
    [2016] Towards an Understanding of the Performance of Associative Copolymers in porous Media, paper presented at the Oil Field Chemistry Symposium, Geilo, Norway, 13–15 March.
     [Google Scholar]
  11. Reichenbach-Klinke, R., Stavland, A., Strand, D., Berland, H., Langlotz, B. and Brodt, G.
    [2016] Can Associative Polymers Reduce the Residual Oil Saturation. Paper SPE 179801-MS presented at the SPE EOR Conference at Oil and Gas West Asia, Muscat, Oman21–23 March.
     [Google Scholar]
  12. Rotureau, E., Dellacherie, E., Durand, A.
    [2006] Viscosity of aqueous solutions of polysaccharides and hydrophobically modified polysaccharides : Application of Fedors equation. Eur. Polym. J. 42, 1086–1092.
     [Google Scholar]
  13. Sheng, J. J.
    [2011] Modern Chemical Enhanced Oil Recovery, Elsevier.
     [Google Scholar]
  14. Zhu, Y., Xu, Y., Huang, G.
    [2013] Synthesis and Aqueous Solution Properties of Novel Thermosensitive Polyacrylamide Derivatives. J. Appl. Polym. Sci. 130, 766–775.
     [Google Scholar]
http://instance.metastore.ingenta.com/content/papers/10.3997/2214-4609.201700285
Loading
Temperature-switchable Polymer for Enhanced Oil Recovery
Conference Proceedings 2017, 1 (2017); https://doi.org/10.3997/2214-4609.201700285
/content/papers/10.3997/2214-4609.201700285
/content/papers/10.3997/2214-4609.201700285
Loading

Data & Media loading...

Most Cited This Month Most Cited RSS feed

This is a required field
Please enter a valid email address
Approval was a Success
Invalid data
An Error Occurred
Approval was partially successful, following selected items could not be processed due to error